Nuts

Grade 2H nuts are recommended for use with bolts in high-pressure and high-temperature service
Grade-2H nuts are heat treated by quenching in a liquid medium from a temp above the transformation temp
Rockwell C24 - C38
150,000 psi proof load
Hot dip galvanizing is generally the most effective way to apply a sufficient thickness of zinc to threaded fasteners for zinc to serve as a corrosion protection in harsh enviroments.

Grade 2H nuts are recommended for use with bolts in high-pressure and high-temperature service
Grade-2H nuts are heat treated by quenching in a liquid medium from a temp above the transformation temp
Rockwell C24 - C38
150,000 psi proof load
Hot dip galvanizing is generally the most effective way to apply a sufficient thickness of zinc to threaded fasteners for zinc to serve as a corrosion protection in harsh enviroments.

Grade 2H nuts are recommended for use with bolts in high-pressure and high-temperature service
Grade-2H nuts are heat treated by quenching in a liquid medium from a temp above the transformation temp
Rockwell C24 - C38
150,000 psi proof load
Hot dip galvanizing is generally the most effective way to apply a sufficient thickness of zinc to threaded fasteners for zinc to serve as a corrosion protection in harsh enviroments.

Grade 2H nuts are recommended for use with bolts in high-pressure and high-temperature service
Grade-2H nuts are heat treated by quenching in a liquid medium from a temp above the transformation temp
Rockwell C24 - C38
150,000 psi proof load

Grade 2H nuts are recommended for use with bolts in high-pressure and high-temperature service
Grade-2H nuts are heat treated by quenching in a liquid medium from a temp above the transformation temp
Rockwell C24 - C38
150,000 psi proof load